Massive vanadium additions as hard phases in powder metallurgy high-speed steels(PM HSS)lead to higher cost and bad machinability.In this study,ultrahigh alloy PM HSS with CPM121(10W-5Mo-4Cr-10V-9Co,wt.%)as the basic ...Massive vanadium additions as hard phases in powder metallurgy high-speed steels(PM HSS)lead to higher cost and bad machinability.In this study,ultrahigh alloy PM HSS with CPM121(10W-5Mo-4Cr-10V-9Co,wt.%)as the basic composition,was directly compacted and activation sintered with near-full density(>99.0%)using pre-oxidized and ball-mixed element and carbide powders.Niobium-alloyed steels(w(V)+w(Nb)=10 wt.%)show higher hardness and wear resistance,superior secondary-hardening ability and temper resistance.But excess niobium addition(>5 wt.%)leads to coarsened carbides and deteriorated toughness.EPMA results proved that niobium tends to distribute in MC carbides and forces element W to form M6C and WC carbides.Further,the role of rotary forging on properties of niobium-alloyed steels(S3)was researched.After rotary forging with deformation of 40%,the bending strength and fracture toughness of niobium-alloyed steels could be further improved by 20.74%and 43.86%compared with those of sample S3 without rotary forging,respectively.展开更多
基金Projects(51771237,51704257)supported by the National Natural Science Foundation of ChinaProject(2019JJ60019)supported by the Joint Fund of Hunan Province,ChinaProject(17QDZ25)supported by the School Level Fund of Xiangtan University,China。
文摘Massive vanadium additions as hard phases in powder metallurgy high-speed steels(PM HSS)lead to higher cost and bad machinability.In this study,ultrahigh alloy PM HSS with CPM121(10W-5Mo-4Cr-10V-9Co,wt.%)as the basic composition,was directly compacted and activation sintered with near-full density(>99.0%)using pre-oxidized and ball-mixed element and carbide powders.Niobium-alloyed steels(w(V)+w(Nb)=10 wt.%)show higher hardness and wear resistance,superior secondary-hardening ability and temper resistance.But excess niobium addition(>5 wt.%)leads to coarsened carbides and deteriorated toughness.EPMA results proved that niobium tends to distribute in MC carbides and forces element W to form M6C and WC carbides.Further,the role of rotary forging on properties of niobium-alloyed steels(S3)was researched.After rotary forging with deformation of 40%,the bending strength and fracture toughness of niobium-alloyed steels could be further improved by 20.74%and 43.86%compared with those of sample S3 without rotary forging,respectively.