Understanding the mechanism of progressive debonding of bolts is of great significance for underground safety.In this paper,both laboratory experiment and numerical simulation of the pull-out tests were performed.The ...Understanding the mechanism of progressive debonding of bolts is of great significance for underground safety.In this paper,both laboratory experiment and numerical simulation of the pull-out tests were performed.The experimental pull-out test specimens were prepared using cement mortar material,and a relationship between the pull-out strength of the bolt and the uniaxial compressive strength(UCS)of cement mortar material specimen was established.The locations of crack developed in the pull-out process were identified using the acoustic emission(AE)technique.The pull-out test was reproduced using 2D Particle Flow Code(PFC^(2D))with calibrated parameters.The experimental results show that the axial displacement of the cement mortar material at the peak load during the test was approximately 5 mm for cement-based grout of all strength.In contrast,the peak load of the bolt increased with the UCS of the confining medium.Under peak load,cracks propagated to less than one half of the anchorage length,indicating a lag between crack propagation and axial bolt load transmission.The simulation results show that the dilatation between the bolt and the rock induced cracks and extended the force field along the anchorage direction;and,it was identified as the major contributing factor for the pull-out failure of rock bolt.展开更多
Bedrock and concrete lining are typical composite structures in the engineering field and the stability of the geological body and engineering body is directly connected to the mechanical properties of the composite b...Bedrock and concrete lining are typical composite structures in the engineering field and the stability of the geological body and engineering body is directly connected to the mechanical properties of the composite body.Under this background,the study provides the transverse isotropic equivalent model of concrete-granite double-layer composite based on the notion of strain energy equivalence.Assuming that the strength failure of concrete and granite meets the Mohr-Coulomb criterion,then the strength failure model of the combined body considering the joint roughness coefficient(JRC)is derived,and the influences of JRC,the height ratio of concrete to granite,and confining pressure on the strength failure characteristics of the combined body are emphatically analyzed.Finally,the model applicability is illustrated by the uniaxial and triaxial compression tests on concrete monomer,granite monomer and concretegranite composite samples(CGCSs)with different JRCs.The results revealed that the compressive strength of the composite is closer to the concrete with lower strength in the combined body under different confining pressures.Adding interface roughness causes to raise the compressive strength of the composite due to interfacial adhesion between concrete and granite,and a slowing growth trend is observed in compressive strength as roughness.The model can provide a certain reference for the stability design and evaluation of engineering rock mass.展开更多
This paper investigates mechanical behaviours of sandstone during post-peak cyclic loading and unloading subjected to hydromechanical coupling effect, confirming the peak and residual strengths reduction laws of sands...This paper investigates mechanical behaviours of sandstone during post-peak cyclic loading and unloading subjected to hydromechanical coupling effect, confirming the peak and residual strengths reduction laws of sandstone with water pressure, and revealing the influence of water pressure on the upper limit stress and deformation characteristics of sandstone during post-peak cyclic loading and unloading.Regarding the rock strength, the experimental study confirms that the peak strength σ_(p) and residual strength σ_(r) decrease as water pressure P increases. Especially, the normalized strength parameters σ_(p)/σ_(pk) and σ_(r)/σ_(re) was negatively and linearly correlated with the P/σ_(3). Moreover, the Hoek-Brown strength criterion can be applied to describe the relationship between effective peak strength and effective confining stress. During post-peak cyclic loading and unloading, both the upper limit stress σ_(p(i)) and crack damage threshold stress σ_(cd(i)) of each cycle tend to decrease with the increasing cycle number. A hysteresis loop exists among the loading and unloading stress–strain curves, indicating the unloading deformation modulus E_(unload) is larger than the loading deformation modulus E_(load). Based on experimental results,a post-peak strength prediction model related to water pressure and plastic shear strain is established.展开更多
基金Financial supports for this work,provided by the National Natural Science Foundation of China(No.41974164)the Scientific Research Startup Fund for High Level Talents Introduced by Anhui University of Science and Technology(No.2021yjrc16)the Chinese Government Scholarship(No.201906420030),are gratefully acknowledged.
文摘Understanding the mechanism of progressive debonding of bolts is of great significance for underground safety.In this paper,both laboratory experiment and numerical simulation of the pull-out tests were performed.The experimental pull-out test specimens were prepared using cement mortar material,and a relationship between the pull-out strength of the bolt and the uniaxial compressive strength(UCS)of cement mortar material specimen was established.The locations of crack developed in the pull-out process were identified using the acoustic emission(AE)technique.The pull-out test was reproduced using 2D Particle Flow Code(PFC^(2D))with calibrated parameters.The experimental results show that the axial displacement of the cement mortar material at the peak load during the test was approximately 5 mm for cement-based grout of all strength.In contrast,the peak load of the bolt increased with the UCS of the confining medium.Under peak load,cracks propagated to less than one half of the anchorage length,indicating a lag between crack propagation and axial bolt load transmission.The simulation results show that the dilatation between the bolt and the rock induced cracks and extended the force field along the anchorage direction;and,it was identified as the major contributing factor for the pull-out failure of rock bolt.
基金The authors would like to acknowledge financial supports from the National Natural Science Foundation of China(Nos.41941019 and 52274145)Department of Science and Technology of Shaanxi Province(No.2021TD-55)+2 种基金“111”Center,Program of the Ministry of Education of China(No.B18046)Natural Science Foundation of Shaanxi Province(No.2020JQ-373)the Fundamental Research Funds for the Central Universities,CHD(No.300102261101).
文摘Bedrock and concrete lining are typical composite structures in the engineering field and the stability of the geological body and engineering body is directly connected to the mechanical properties of the composite body.Under this background,the study provides the transverse isotropic equivalent model of concrete-granite double-layer composite based on the notion of strain energy equivalence.Assuming that the strength failure of concrete and granite meets the Mohr-Coulomb criterion,then the strength failure model of the combined body considering the joint roughness coefficient(JRC)is derived,and the influences of JRC,the height ratio of concrete to granite,and confining pressure on the strength failure characteristics of the combined body are emphatically analyzed.Finally,the model applicability is illustrated by the uniaxial and triaxial compression tests on concrete monomer,granite monomer and concretegranite composite samples(CGCSs)with different JRCs.The results revealed that the compressive strength of the composite is closer to the concrete with lower strength in the combined body under different confining pressures.Adding interface roughness causes to raise the compressive strength of the composite due to interfacial adhesion between concrete and granite,and a slowing growth trend is observed in compressive strength as roughness.The model can provide a certain reference for the stability design and evaluation of engineering rock mass.
基金supported by the National Natural Science Foundation of China(Nos.52274118 and 52274145)the Construction Project of Chenzhou National Sustainable Development Agenda Innovation Demonstration Zone(No.2021sfQ18).
文摘This paper investigates mechanical behaviours of sandstone during post-peak cyclic loading and unloading subjected to hydromechanical coupling effect, confirming the peak and residual strengths reduction laws of sandstone with water pressure, and revealing the influence of water pressure on the upper limit stress and deformation characteristics of sandstone during post-peak cyclic loading and unloading.Regarding the rock strength, the experimental study confirms that the peak strength σ_(p) and residual strength σ_(r) decrease as water pressure P increases. Especially, the normalized strength parameters σ_(p)/σ_(pk) and σ_(r)/σ_(re) was negatively and linearly correlated with the P/σ_(3). Moreover, the Hoek-Brown strength criterion can be applied to describe the relationship between effective peak strength and effective confining stress. During post-peak cyclic loading and unloading, both the upper limit stress σ_(p(i)) and crack damage threshold stress σ_(cd(i)) of each cycle tend to decrease with the increasing cycle number. A hysteresis loop exists among the loading and unloading stress–strain curves, indicating the unloading deformation modulus E_(unload) is larger than the loading deformation modulus E_(load). Based on experimental results,a post-peak strength prediction model related to water pressure and plastic shear strain is established.