An azo metal chelate compound with push pull electronic system was synthesized. Smooth thin films were prepared by spin coating. The absorption, transmission and reflection spectra of the films were measured. The opti...An azo metal chelate compound with push pull electronic system was synthesized. Smooth thin films were prepared by spin coating. The absorption, transmission and reflection spectra of the films were measured. The optical constant (complex refractive index N=n +i k ) of the film was determined using scanning ellipsometer, and the complex dielectric function ε as well as absorption coefficient α were then calculated. Dynamic optical recording test indicated that the azo metal chelate dye was a promising candidate as optical recording medium.展开更多
A novel azo derivative,α-（2-azoxyisoxazole)-β-diketone derivative (ADD),and its copper (Ⅱ） and nickel （Ⅱ） complex (CuADD and NiADD) films have been prepared respectively by spin-coated method.The absorption sp...A novel azo derivative,α-（2-azoxyisoxazole)-β-diketone derivative (ADD),and its copper (Ⅱ） and nickel （Ⅱ） complex (CuADD and NiADD) films have been prepared respectively by spin-coated method.The absorption spectra of the films on a K9 glass substrate in the 300-800 nm wavelength region have been measured.The optical constants (complex refractive index N=n+iκ） and thickness of the complex films on a single-crystal silicon substrate in the 300-600nm wavelength region have been investigated on an improved rotating analyser-polariser (RAP) type of scanning ellipsometer,and the dielectric constants ε（ε=ε1+iε2),absorption coefficients α as well as reflectance R of the films were calculated.It is found that the absorption maxima of the ADD,CuADD and NiADD films are at 324nm,372nm and 385nm,respectively,and small absorption values and steep absorption band edges of the CuADD and NiADD films are observed at the 405nm side;The CuADD and NiADD films give high n values of 2.08 and 1.98,and low κ values of 0.2 and 0.28,respectively,at 405nm,and their thicknesses are in the range of 130-150nm;the high reflectivity of 58.5% and 45.5% of the CuADD and NiADD films with Ag as a reflective layer were obtained at the film thicknesses of 70 nm and 80nm respectively.These results show that the novel CuADD and NiADD films seem to be a very promising organic recording material for the next generation of high density digital versatile disc-recordable (HD-DVD-R) systems that use a high numerical aperture of 0.85 at 405nm wavelength.展开更多
Fe：BiOx films are fabricated on K9 glass substrates by rf-magnetron sputtering of a BiFeO target under argon atmosphere with increasing sputtering power from 80 to 200 W at room temperature. It is found that the thin...Fe：BiOx films are fabricated on K9 glass substrates by rf-magnetron sputtering of a BiFeO target under argon atmosphere with increasing sputtering power from 80 to 200 W at room temperature. It is found that the thin films grown at the sputtering power of 160 W can be formed at an appropriate deposition rate and have an improved surface morphology. The XPS result reveals that the films investigated are comprised of Bi, Fe and O elements. A typical XRD pattern shows that no phase transition occurs in the films up to 400℃. The results of the blue laser recording test demonstrate that the Fe：BiOx films have good writing sensitivity for blue laser beam （406.7nm） and good stability after reading 10000 times. The recording marks of 200nm or less are obtained. These results indicate that the introduction of Fe into BiOx films can reduce the mark size and improve the stability of the films.展开更多
The three-photon absorption （3PA） properties of two thiophene-fluorene derivatives （abbreviated as MOTFTBr and ATFTBr） have been determined by using a Q-switched Nd：YAG laser pumped with 38ps pulses at 1064nm in ...The three-photon absorption （3PA） properties of two thiophene-fluorene derivatives （abbreviated as MOTFTBr and ATFTBr） have been determined by using a Q-switched Nd：YAG laser pumped with 38ps pulses at 1064nm in DMF. The measured 3PA cross-sections are 152×10^-78cm^6s^2 and 139× 10^-78cm^6s^2, respectively. The optimized structures were obtained by AM1 calculations and the results indicate that these two molecules show nonplanar structures, and attaching different donors has different effects on the molecular structure. The charge density distributions during the excitation were also systematically studied by using AM1 method. In addition, an obvious optical power limiting effect induced by 3PA has been demonstrated for both derivatives.展开更多
Scanning tunneling microscope (STM) is used to investigate the optical disc.The areas with and without data stampers are all observed carefully. Three-dimensional images of the disc surface clearly demonstrate the per...Scanning tunneling microscope (STM) is used to investigate the optical disc.The areas with and without data stampers are all observed carefully. Three-dimensional images of the disc surface clearly demonstrate the period, depth of the grooves and the shape of data stampers. Some phenomena of STM imaging are also discussed.展开更多
SbOx thin films are deposited by reactive dc-magnetron sputtering from an antimony metal target in Ar＋O2 with the relative O2 content 7%. It is found that the as-deposited films can represent a two-component system c...SbOx thin films are deposited by reactive dc-magnetron sputtering from an antimony metal target in Ar＋O2 with the relative O2 content 7%. It is found that the as-deposited films can represent a two-component system comprising amorphous Sb and amorphous Sb2 O3. The crystallization of Sb is responsible for the changes of optical properties of the films. The results of the static test show that the SbOx thin films have good writing sensitivity for blue laser beams and the recording marks are very clear and circular. High reflectivity contrast of about 41% is obtained at a writing power 6mW and writing pulse width 300ns. In addition, the films show a good stability after reading 10000 times.展开更多
文摘An azo metal chelate compound with push pull electronic system was synthesized. Smooth thin films were prepared by spin coating. The absorption, transmission and reflection spectra of the films were measured. The optical constant (complex refractive index N=n +i k ) of the film was determined using scanning ellipsometer, and the complex dielectric function ε as well as absorption coefficient α were then calculated. Dynamic optical recording test indicated that the azo metal chelate dye was a promising candidate as optical recording medium.
文摘A novel azo derivative,α-（2-azoxyisoxazole)-β-diketone derivative (ADD),and its copper (Ⅱ） and nickel （Ⅱ） complex (CuADD and NiADD) films have been prepared respectively by spin-coated method.The absorption spectra of the films on a K9 glass substrate in the 300-800 nm wavelength region have been measured.The optical constants (complex refractive index N=n+iκ） and thickness of the complex films on a single-crystal silicon substrate in the 300-600nm wavelength region have been investigated on an improved rotating analyser-polariser (RAP) type of scanning ellipsometer,and the dielectric constants ε（ε=ε1+iε2),absorption coefficients α as well as reflectance R of the films were calculated.It is found that the absorption maxima of the ADD,CuADD and NiADD films are at 324nm,372nm and 385nm,respectively,and small absorption values and steep absorption band edges of the CuADD and NiADD films are observed at the 405nm side;The CuADD and NiADD films give high n values of 2.08 and 1.98,and low κ values of 0.2 and 0.28,respectively,at 405nm,and their thicknesses are in the range of 130-150nm;the high reflectivity of 58.5% and 45.5% of the CuADD and NiADD films with Ag as a reflective layer were obtained at the film thicknesses of 70 nm and 80nm respectively.These results show that the novel CuADD and NiADD films seem to be a very promising organic recording material for the next generation of high density digital versatile disc-recordable (HD-DVD-R) systems that use a high numerical aperture of 0.85 at 405nm wavelength.
基金Supported by the National Natural Science Foundation of China under Grant No 50672108 and 60644002.
文摘Fe：BiOx films are fabricated on K9 glass substrates by rf-magnetron sputtering of a BiFeO target under argon atmosphere with increasing sputtering power from 80 to 200 W at room temperature. It is found that the thin films grown at the sputtering power of 160 W can be formed at an appropriate deposition rate and have an improved surface morphology. The XPS result reveals that the films investigated are comprised of Bi, Fe and O elements. A typical XRD pattern shows that no phase transition occurs in the films up to 400℃. The results of the blue laser recording test demonstrate that the Fe：BiOx films have good writing sensitivity for blue laser beam （406.7nm） and good stability after reading 10000 times. The recording marks of 200nm or less are obtained. These results indicate that the introduction of Fe into BiOx films can reduce the mark size and improve the stability of the films.
基金Project supported by the National Natural Science Foundation of China （Grant No 60207005） and the Shanghai Science ＆ Technology Development Foundation （Grant No 012261068）.
文摘The three-photon absorption （3PA） properties of two thiophene-fluorene derivatives （abbreviated as MOTFTBr and ATFTBr） have been determined by using a Q-switched Nd：YAG laser pumped with 38ps pulses at 1064nm in DMF. The measured 3PA cross-sections are 152×10^-78cm^6s^2 and 139× 10^-78cm^6s^2, respectively. The optimized structures were obtained by AM1 calculations and the results indicate that these two molecules show nonplanar structures, and attaching different donors has different effects on the molecular structure. The charge density distributions during the excitation were also systematically studied by using AM1 method. In addition, an obvious optical power limiting effect induced by 3PA has been demonstrated for both derivatives.
文摘Scanning tunneling microscope (STM) is used to investigate the optical disc.The areas with and without data stampers are all observed carefully. Three-dimensional images of the disc surface clearly demonstrate the period, depth of the grooves and the shape of data stampers. Some phenomena of STM imaging are also discussed.
基金Supported by the National High-Technology Development Programme of China under Grant No 2004AA31G230, and the National Natural Science Foundation of China under Grant Nos 50672108 and 60644002.
文摘SbOx thin films are deposited by reactive dc-magnetron sputtering from an antimony metal target in Ar＋O2 with the relative O2 content 7%. It is found that the as-deposited films can represent a two-component system comprising amorphous Sb and amorphous Sb2 O3. The crystallization of Sb is responsible for the changes of optical properties of the films. The results of the static test show that the SbOx thin films have good writing sensitivity for blue laser beams and the recording marks are very clear and circular. High reflectivity contrast of about 41% is obtained at a writing power 6mW and writing pulse width 300ns. In addition, the films show a good stability after reading 10000 times.