Yb：Sc2O3 transparent ceramics are fabricated by a conventional ceramic process and sintering in H2 atmosphere. The room-temperature spectroscopic properties are investigated, and the Raman spectrum shows an obvious v...Yb：Sc2O3 transparent ceramics are fabricated by a conventional ceramic process and sintering in H2 atmosphere. The room-temperature spectroscopic properties are investigated, and the Raman spectrum shows an obvious vibration characteristic band centred at 415 cm-1. There are three broad absorption bands around 891, 937, and 971 nm, respectively. The strongest emission peak is centred at 1.04 μm with a broad bandwidth （11 nm） and an emission cross-section of 1.8×10^-20 cm^2. The gain coefficient implies a possible laser ability in a range from 990 nm to 1425 nm. The energy-level structure shows that Yb：Sc2O3 ceramics have large Stark splitting at the ground state level due to their strong crystal field. All the results show that Yb：Sc2O3 transparent ceramics are a promising material for short pulse lasers.展开更多
Highly transparent Yb,Ho doped（YLa）2O3 ceramic was fabricated by conventional ceramic processing with nanopowders.The absorption and emission spectra of the ceramic was investigated.The energy transfer mechanism bet...Highly transparent Yb,Ho doped（YLa）2O3 ceramic was fabricated by conventional ceramic processing with nanopowders.The absorption and emission spectra of the ceramic was investigated.The energy transfer mechanism between Yb3＋ and Ho3＋ was also discussed.The strong emission band around 2 μm indicated that the Yb-Ho：（Y 0.90 La 0.10）2O3 transparent ceramic is a promising gain medium for the generation of 2 μm laser emissions.The laser operation of Yb-Ho co-doped（YLa）2O3 ceramic at 2.1 μm is first reported.展开更多
This paper reports that polycrystalline （α-Al2O3：C ceramics are fabricated by conventional ceramics process. The excitation, emission spectra, thermoluminescence （TL） and optical stimulated luminescence （OSL） ...This paper reports that polycrystalline （α-Al2O3：C ceramics are fabricated by conventional ceramics process. The excitation, emission spectra, thermoluminescence （TL） and optical stimulated luminescence （OSL） of α-Al2O3：C polycrystalline ceramics are investigated. There exists 410nm maximum emission peak which is caused by recombination of an electron with F＋ centre to produce an excited F centre. The samples show three clear TL glow peaks at 405, 493 and 610 K. The attenuation constant of exponentially decaying fast component （τ1） and slow component（τ2） of OSL curve are 8.43s and 41.73s, respectively. Those fluorescence and thermoluminescence characteristics are similar with α-Al2O3：C crystal.展开更多
Ce3＋-doped yttrium lanthanum oxide （Y0.9La0.1）2O3 transparent ceramics is fabricated with nanopowders and sintered in H2 atmosphere. The spectral properties of Ce：（Y0.9La0.1）2O3 transparent ceramics are investig...Ce3＋-doped yttrium lanthanum oxide （Y0.9La0.1）2O3 transparent ceramics is fabricated with nanopowders and sintered in H2 atmosphere. The spectral properties of Ce：（Y0.9La0.1）2O3 transparent ceramics are investigated. There appear two characteristic absorption peaks of Ce3＋ ions at 230~nm and 400~nm, separately. It is found that Ce3＋ ions can efficiently produce emission at 384~nm from （Y0.9La0.1）2O3 transparent ceramic host, while the emission is completely quenched in Re2O3 （Re=Y, Lu, La） host materials.展开更多
基金supported by the Key Basic Research Project of Science and Technology Commission of Shanghai, China (Grant No. 09JC1406500)
文摘Yb：Sc2O3 transparent ceramics are fabricated by a conventional ceramic process and sintering in H2 atmosphere. The room-temperature spectroscopic properties are investigated, and the Raman spectrum shows an obvious vibration characteristic band centred at 415 cm-1. There are three broad absorption bands around 891, 937, and 971 nm, respectively. The strongest emission peak is centred at 1.04 μm with a broad bandwidth （11 nm） and an emission cross-section of 1.8×10^-20 cm^2. The gain coefficient implies a possible laser ability in a range from 990 nm to 1425 nm. The energy-level structure shows that Yb：Sc2O3 ceramics have large Stark splitting at the ground state level due to their strong crystal field. All the results show that Yb：Sc2O3 transparent ceramics are a promising material for short pulse lasers.
基金Project supported by the National Natural Science Foundation of China (Grant No. 60578041)the Sciences and Technology Commission Foundation of Shanghai,China (Grant No. 08520707300)+1 种基金the Key Basic Research Project of Science and Technology Commission of Shanghai,China (Grant No. 09JC1406500)the Graduate Student Innovation Fund of Shanghai University,China (Grant No. SHUCX120058)
文摘Highly transparent Yb,Ho doped（YLa）2O3 ceramic was fabricated by conventional ceramic processing with nanopowders.The absorption and emission spectra of the ceramic was investigated.The energy transfer mechanism between Yb3＋ and Ho3＋ was also discussed.The strong emission band around 2 μm indicated that the Yb-Ho：（Y 0.90 La 0.10）2O3 transparent ceramic is a promising gain medium for the generation of 2 μm laser emissions.The laser operation of Yb-Ho co-doped（YLa）2O3 ceramic at 2.1 μm is first reported.
基金supported by the National Natural Science Foundation of China (Grant No. 60578041)the Sciences and Technology Commission Foundation of Shanghai,China (Grant No. 08520707300)the Key Basic Research Project of Science and Technology of Shanghai (Grant No. 09JC1406500)
文摘This paper reports that polycrystalline （α-Al2O3：C ceramics are fabricated by conventional ceramics process. The excitation, emission spectra, thermoluminescence （TL） and optical stimulated luminescence （OSL） of α-Al2O3：C polycrystalline ceramics are investigated. There exists 410nm maximum emission peak which is caused by recombination of an electron with F＋ centre to produce an excited F centre. The samples show three clear TL glow peaks at 405, 493 and 610 K. The attenuation constant of exponentially decaying fast component （τ1） and slow component（τ2） of OSL curve are 8.43s and 41.73s, respectively. Those fluorescence and thermoluminescence characteristics are similar with α-Al2O3：C crystal.
基金supported by the National Natural Science Foundation of China (Grant No. 60578041)the Shanghai Leading Academic Disciplines (Grant No. S30107)
文摘Ce3＋-doped yttrium lanthanum oxide （Y0.9La0.1）2O3 transparent ceramics is fabricated with nanopowders and sintered in H2 atmosphere. The spectral properties of Ce：（Y0.9La0.1）2O3 transparent ceramics are investigated. There appear two characteristic absorption peaks of Ce3＋ ions at 230~nm and 400~nm, separately. It is found that Ce3＋ ions can efficiently produce emission at 384~nm from （Y0.9La0.1）2O3 transparent ceramic host, while the emission is completely quenched in Re2O3 （Re=Y, Lu, La） host materials.