To improve the ablation resistance of carbon/carbon(C/C)composites,a SiC/ZrC-ZrB2 double layer coating was fabricated by pack cementation and slurry-sintering method.The ablation resistance of the SiC/ZrC-ZrB2 coating...To improve the ablation resistance of carbon/carbon(C/C)composites,a SiC/ZrC-ZrB2 double layer coating was fabricated by pack cementation and slurry-sintering method.The ablation resistance of the SiC/ZrC-ZrB2 coating was tested under plasma flame above 2300°C.The results indicate that the SiC/ZrC-ZrB2 double layer coating exhibits superior ablation resistance than the ZrC-ZrB2 single layer coating.After being ablated under the plasma flame for 20 s,the mass and linear ablation rates of the ZrC-ZrB2 coating are 0.89 mg/s and 15.3μm/s,while those for SiC/ZrC-ZrB2 coating are 0.09 mg/s and 24.15μm/s,respectively.During ablation,the SiC inner layer can generate SiO2 glass and result in the formation of ZrO2-SiO2 molten film.Compared with the ZrO2 molten film formed on the ZrC-ZrB2 coating surface,the ZrO2-SiO2 molten film with lower oxygen diffusion rate and viscosity enables the SiC/ZrC-ZrB2 coating to have better self-healing ability.Therefore,the enhanced ablation resistance of the SiC/ZrC-ZrB2 coating can be attributed to the formation of dense ZrO2-SiO2 molten film under the plasma flame.展开更多
基金Project(51304249)supported by the National Natural Science Foundation of ChinaProject(14JJ3023)supported by the Science Foundation of Hunan Province,China。
文摘To improve the ablation resistance of carbon/carbon(C/C)composites,a SiC/ZrC-ZrB2 double layer coating was fabricated by pack cementation and slurry-sintering method.The ablation resistance of the SiC/ZrC-ZrB2 coating was tested under plasma flame above 2300°C.The results indicate that the SiC/ZrC-ZrB2 double layer coating exhibits superior ablation resistance than the ZrC-ZrB2 single layer coating.After being ablated under the plasma flame for 20 s,the mass and linear ablation rates of the ZrC-ZrB2 coating are 0.89 mg/s and 15.3μm/s,while those for SiC/ZrC-ZrB2 coating are 0.09 mg/s and 24.15μm/s,respectively.During ablation,the SiC inner layer can generate SiO2 glass and result in the formation of ZrO2-SiO2 molten film.Compared with the ZrO2 molten film formed on the ZrC-ZrB2 coating surface,the ZrO2-SiO2 molten film with lower oxygen diffusion rate and viscosity enables the SiC/ZrC-ZrB2 coating to have better self-healing ability.Therefore,the enhanced ablation resistance of the SiC/ZrC-ZrB2 coating can be attributed to the formation of dense ZrO2-SiO2 molten film under the plasma flame.