Surface tension of calcium aluminate refining slag was measured by the Slide method at 1823 K.Based on different levels of the MgO content and the mass ratio of CaO to Al_2O_3,the effects of MgO content and the mass r...Surface tension of calcium aluminate refining slag was measured by the Slide method at 1823 K.Based on different levels of the MgO content and the mass ratio of CaO to Al_2O_3,the effects of MgO content and the mass ratio of CaO to Al_2O_3 on surface tension were investigated.The results indicate that surface tension decreased with increasing MgO content(from 0 to 4.86%),followed by an increase with further increasing MgO content up to 11.33%.The trend that surface tension changed with the mass ratio of CaO to Al_2O_3 was the same as the trend that surface tension changed with the MgO content.The surface tension was varied from 0.617 N/m to 0.710 N/m,for the mass ratio of CaO to Al_2O_3 varying between 0.60 and 1.28.An attempt was made to estimate surface tension of CaO-Al_2O_3-MgO slag and its sub-system,and the application showed that the model worked well.展开更多
Deep level donor＇s ionization behavior of passive film formed on the surface of stainless steel was investigated by Mott-Schottky plots. It is indicated that transformation process of deep level donors＇ ionization b...Deep level donor＇s ionization behavior of passive film formed on the surface of stainless steel was investigated by Mott-Schottky plots. It is indicated that transformation process of deep level donors＇ ionization behavior of passive film on surface of stainless steel can be divided into 4 stages with rising immersion time. At the initial immersion stage （10 min）, Fe（II） located in the octahedral sites of the unit cell is not ionized and the deep level does not appear in Mott-Schottky plots. At the second stage （9-38 h）, Fe（II） located in the octahedral sites starts to be ionized, which results in deep level donors＇ generation and density of deep level donors almost is constant with augmenting immersion time but the thickness of space charge layer is more and more thicker with rising immersion time. At the third stage （48 h-12 d）, density of deep level donors rises with increasing immersion time and the thickness of passive films space charge layer decreases. At last stage （above 23 d）, both the space charge layer＇s thickness and density of deep level donors are no longer changed with increasing immersion time. In the overall immersion stage, the shallow level donors＇ density is invariable all the time. The mechanism of deep level donor＇s ionization can be the generation of metal vacancies, which results in crystal lattice＇s aberration and the aberration energy urges the ionization of Fe（ II ） in octahedral sites.展开更多
基金Project(51204115)supported by the National Natural Science Foundation of ChinaProject(BK20130308)supported by the Basic Research Program of Jiangsu Province,ChinaProject(2014M561710)supported by China Postdoctoral Science Foundation
文摘Surface tension of calcium aluminate refining slag was measured by the Slide method at 1823 K.Based on different levels of the MgO content and the mass ratio of CaO to Al_2O_3,the effects of MgO content and the mass ratio of CaO to Al_2O_3 on surface tension were investigated.The results indicate that surface tension decreased with increasing MgO content(from 0 to 4.86%),followed by an increase with further increasing MgO content up to 11.33%.The trend that surface tension changed with the mass ratio of CaO to Al_2O_3 was the same as the trend that surface tension changed with the MgO content.The surface tension was varied from 0.617 N/m to 0.710 N/m,for the mass ratio of CaO to Al_2O_3 varying between 0.60 and 1.28.An attempt was made to estimate surface tension of CaO-Al_2O_3-MgO slag and its sub-system,and the application showed that the model worked well.
基金Foundation item: Projects(50571059, 50615024 ) supported by the National Natural Science Foundation of ChinaProject(NCET-07-0536) supported by Program for New Century Excellent Talents in UniversityProject(IRT0739) supported by Program for Innovative Research Team in University
文摘Deep level donor＇s ionization behavior of passive film formed on the surface of stainless steel was investigated by Mott-Schottky plots. It is indicated that transformation process of deep level donors＇ ionization behavior of passive film on surface of stainless steel can be divided into 4 stages with rising immersion time. At the initial immersion stage （10 min）, Fe（II） located in the octahedral sites of the unit cell is not ionized and the deep level does not appear in Mott-Schottky plots. At the second stage （9-38 h）, Fe（II） located in the octahedral sites starts to be ionized, which results in deep level donors＇ generation and density of deep level donors almost is constant with augmenting immersion time but the thickness of space charge layer is more and more thicker with rising immersion time. At the third stage （48 h-12 d）, density of deep level donors rises with increasing immersion time and the thickness of passive films space charge layer decreases. At last stage （above 23 d）, both the space charge layer＇s thickness and density of deep level donors are no longer changed with increasing immersion time. In the overall immersion stage, the shallow level donors＇ density is invariable all the time. The mechanism of deep level donor＇s ionization can be the generation of metal vacancies, which results in crystal lattice＇s aberration and the aberration energy urges the ionization of Fe（ II ） in octahedral sites.