Diamond films were deposited on high-speed steel substrates by hot filament chemical vapor deposition （HFCVD） method. To minimize the early formation of graphite and to enhance the diamond film adhesion, a WC-Co coa...Diamond films were deposited on high-speed steel substrates by hot filament chemical vapor deposition （HFCVD） method. To minimize the early formation of graphite and to enhance the diamond film adhesion, a WC-Co coating was used as an interlayer on the steel substrates by high velocity oxy-fuel spraying. The effects of methane content on nucleation, quality, residual stress and adhesion of diamond films were investigated. The results indicate that the increasing methane content leads to the increase in nucleation density, residual stress, the degradation of quality and adhesion of diamond films. Diamond films deposited on high-speed steel （HSS） substrate with a WC-Co interlayer exhibit high nucleation density and good adhesion under the condition of the methane content initially set to be a higher value （4%, volume fraction） for 30 min, and then reduced to 2% for subsequent growth at pressure of 3 kPa and substrate temperature of 800 ℃.展开更多
基金Project(1343-74236000005) supported by the Innovation Foundation for Postgraduates of Hunan Province, ChinaProject(ZKJ2008001) supported by the Open Fund for Valuable Instruments of Central South University, ChinaProject(2008112048) supported by the Open Fund of State Key Laboratory of Metallurgy, China
文摘Diamond films were deposited on high-speed steel substrates by hot filament chemical vapor deposition （HFCVD） method. To minimize the early formation of graphite and to enhance the diamond film adhesion, a WC-Co coating was used as an interlayer on the steel substrates by high velocity oxy-fuel spraying. The effects of methane content on nucleation, quality, residual stress and adhesion of diamond films were investigated. The results indicate that the increasing methane content leads to the increase in nucleation density, residual stress, the degradation of quality and adhesion of diamond films. Diamond films deposited on high-speed steel （HSS） substrate with a WC-Co interlayer exhibit high nucleation density and good adhesion under the condition of the methane content initially set to be a higher value （4%, volume fraction） for 30 min, and then reduced to 2% for subsequent growth at pressure of 3 kPa and substrate temperature of 800 ℃.