Ni50Mn25Ga20Fe5 ferromagnetic shape memory alloy microwires with diameters of^30-50μm and grain sizes of^2-5μm were prepared by melt-extraction technique.A step-wise chemical ordering annealing was carried out to im...Ni50Mn25Ga20Fe5 ferromagnetic shape memory alloy microwires with diameters of^30-50μm and grain sizes of^2-5μm were prepared by melt-extraction technique.A step-wise chemical ordering annealing was carried out to improve the superelasticity strain and recovery ratio which were hampered by the internal stress,compositional inhomogeneity,and high-density defects in the as-extracted Ni50Mn25Ga20Fe5 microwires.The annealed microwires exhibited enhanced atomic ordering degree,narrow thermal hysteresis,and high saturation magnetization under a low magnetic field.As a result,the annealed microwire showed decreased superelastic critical stress,improved reversibility,and a high superelastic strain(1.9%)with a large recovery ratio(>96%).This kind of filamentous material with superior superelastic effects may be promising materials for minor-devices.展开更多
基金Project supported by the National Natural Science Foundation of China (Grant Nos. 51701099,51801044,and 51671071)the Natural Science Foundation of Heilongjiang Province of China (Grant No. LH2019E091)+1 种基金Fundamental Research Funds in Heilongjiang Provincial Universities,China (Grant No. 135409320)the help of Technology Innovation Center of Agricultural Multi-Dimensional Sensor Information Perception,Heilongjiang Province.
文摘Ni50Mn25Ga20Fe5 ferromagnetic shape memory alloy microwires with diameters of^30-50μm and grain sizes of^2-5μm were prepared by melt-extraction technique.A step-wise chemical ordering annealing was carried out to improve the superelasticity strain and recovery ratio which were hampered by the internal stress,compositional inhomogeneity,and high-density defects in the as-extracted Ni50Mn25Ga20Fe5 microwires.The annealed microwires exhibited enhanced atomic ordering degree,narrow thermal hysteresis,and high saturation magnetization under a low magnetic field.As a result,the annealed microwire showed decreased superelastic critical stress,improved reversibility,and a high superelastic strain(1.9%)with a large recovery ratio(>96%).This kind of filamentous material with superior superelastic effects may be promising materials for minor-devices.