Effects of cold rolling deformation on the microstructure, hardness, and creep behavior of high nitrogen austenitic stainless steel （HNASS） are investigated. Microstructure characterization shows that 70% cold rolli...Effects of cold rolling deformation on the microstructure, hardness, and creep behavior of high nitrogen austenitic stainless steel （HNASS） are investigated. Microstructure characterization shows that 70% cold rolling deformation results in significant refinement of the microstructure of this steel, with its average twin thickness reducing from 6.4 μm to 14 nm. Nanoindentation tests at different strain rates demonstrate that the hardness of the steel with nano-scale twins （nt-HNASS） is about 2 times as high as that of steel with micro-scale twins （mt-HNASS）. The hardness of nt-HNASS exhibits a pronounced strain rate dependence with a strain rate sensitivity （m value） of 0.0319, which is far higher than that of mt-HNASS （m = 0.0029）. nt-HNASS shows more significant load plateaus and a higher creep rate than mt-HNASS. Analysis reveals that higher hardness and larger m value of nt-HNASS arise from stronger strain hardening role, which is caused by the higher storage rate of dislocations and the interactions between dislocations and high density twins. The more significant load plateaus and higher creep rates of nt-HNASS are due to the rapid relaxation of the dislocation structures generated during loading.展开更多
Nanocrystalline Cu with average grain sizes ranging from ～ 24.4 to 131.3 nm were prepared by the electric brushplating technique.Nanoindentation tests were performed within a wide strain rate range,and the creep proc...Nanocrystalline Cu with average grain sizes ranging from ～ 24.4 to 131.3 nm were prepared by the electric brushplating technique.Nanoindentation tests were performed within a wide strain rate range,and the creep process of nanocrystalline Cu during the holding period and its relationship to dislocation and twin structures were examined.It was demonstrated that creep strain and creep strain rate are considerably significant for smaller grain sizes and higher loading strain rates,and are far higher than those predicted by the models of Cobble creep and grain boundary sliding.The analysis based on the calculations and experiments reveals that the significant creep deformation arises from the rapid absorption of high density dislocations stored in the loading regime.Our experiments imply that stored dislocations during loading are highly unstable and dislocation activity can proceed and lead to significant post-loading plasticity.展开更多
The tensile strength and ductility of a high nitrogen nickel-free austenitic stainless steel with solution and cold rolling treatment were investigated by performing tensile tests at different strain rates and at room...The tensile strength and ductility of a high nitrogen nickel-free austenitic stainless steel with solution and cold rolling treatment were investigated by performing tensile tests at different strain rates and at room temperature. The tensile tests demonstrated that this steel exhibits a significant strain rate and cold rolling dependence of the tensile strength and ductility.With the increase of the strain rate from 10^-4s^-1to 1 s^-1, the yield strength and ultimate tensile strength increase and the uniform elongation and total elongation decrease. The analysis of the double logarithmic stress–strain curves showed that this steel exhibits a two-stage strain hardening behavior, which can be well examined and analyzed by using the Ludwigson equation. The strain hardening exponents at low and high strain regions（n2and n1） and the transition strain（εL） decrease with increasing strain rate and the increase of cold rolling RA. Based on the analysis results of the stress–strain curves, the transmission electron microscopy characterization of the microstructure and the scanning electron microscopy observation of the deformation surfaces, the significant strain rate and cold rolling dependence of the strength and ductility of this steel were discussed and connected with the variation in the work hardening and dislocation activity with strain rate and cold rolling.展开更多
Nanocrystalline Cu film with a mirror surface finishing is prepared by the electric brush-plating technique. The as- prepared Cu film exhibits a superhydrophilic behavior with an apparent water contact angle smaller t...Nanocrystalline Cu film with a mirror surface finishing is prepared by the electric brush-plating technique. The as- prepared Cu film exhibits a superhydrophilic behavior with an apparent water contact angle smaller than 10°. A subsequent increase in the water contact angle and a final wetting transition from inherent hydrophilicity with water contact angle smaller than 90° to apparent hydrophobicity with water contact angle larger than 90° are observed when the Cu film is subjected to natural aging. Analysis based on the measurement of hardness with nanoindentation and the theory of the bond-order-length-strength correlation reveals that this wetting variation on the Cu film is attributed to the relaxation of residual stress generated during brush-plating deposition and a surface hydrophobization role associated with the broken bond polarization induced by surface nanostructure.展开更多
基金Project supported by the National Natural Science Foundations of China (Grant Nos.51371089 and 51201068)the National Key Basic Research and Development Program of China (Grant No.2010CB631001)
文摘Effects of cold rolling deformation on the microstructure, hardness, and creep behavior of high nitrogen austenitic stainless steel （HNASS） are investigated. Microstructure characterization shows that 70% cold rolling deformation results in significant refinement of the microstructure of this steel, with its average twin thickness reducing from 6.4 μm to 14 nm. Nanoindentation tests at different strain rates demonstrate that the hardness of the steel with nano-scale twins （nt-HNASS） is about 2 times as high as that of steel with micro-scale twins （mt-HNASS）. The hardness of nt-HNASS exhibits a pronounced strain rate dependence with a strain rate sensitivity （m value） of 0.0319, which is far higher than that of mt-HNASS （m = 0.0029）. nt-HNASS shows more significant load plateaus and a higher creep rate than mt-HNASS. Analysis reveals that higher hardness and larger m value of nt-HNASS arise from stronger strain hardening role, which is caused by the higher storage rate of dislocations and the interactions between dislocations and high density twins. The more significant load plateaus and higher creep rates of nt-HNASS are due to the rapid relaxation of the dislocation structures generated during loading.
基金Project supported by the National Natural Science Foundation of China (Grant Nos. 50771049 and 50871046)the National Basic Research Program of China (Grant No. 2010CB631001)
文摘Nanocrystalline Cu with average grain sizes ranging from ～ 24.4 to 131.3 nm were prepared by the electric brushplating technique.Nanoindentation tests were performed within a wide strain rate range,and the creep process of nanocrystalline Cu during the holding period and its relationship to dislocation and twin structures were examined.It was demonstrated that creep strain and creep strain rate are considerably significant for smaller grain sizes and higher loading strain rates,and are far higher than those predicted by the models of Cobble creep and grain boundary sliding.The analysis based on the calculations and experiments reveals that the significant creep deformation arises from the rapid absorption of high density dislocations stored in the loading regime.Our experiments imply that stored dislocations during loading are highly unstable and dislocation activity can proceed and lead to significant post-loading plasticity.
基金Project supported by the National Natural Science Foundations of China(Grant Nos.51371089 and 51401083)
文摘The tensile strength and ductility of a high nitrogen nickel-free austenitic stainless steel with solution and cold rolling treatment were investigated by performing tensile tests at different strain rates and at room temperature. The tensile tests demonstrated that this steel exhibits a significant strain rate and cold rolling dependence of the tensile strength and ductility.With the increase of the strain rate from 10^-4s^-1to 1 s^-1, the yield strength and ultimate tensile strength increase and the uniform elongation and total elongation decrease. The analysis of the double logarithmic stress–strain curves showed that this steel exhibits a two-stage strain hardening behavior, which can be well examined and analyzed by using the Ludwigson equation. The strain hardening exponents at low and high strain regions（n2and n1） and the transition strain（εL） decrease with increasing strain rate and the increase of cold rolling RA. Based on the analysis results of the stress–strain curves, the transmission electron microscopy characterization of the microstructure and the scanning electron microscopy observation of the deformation surfaces, the significant strain rate and cold rolling dependence of the strength and ductility of this steel were discussed and connected with the variation in the work hardening and dislocation activity with strain rate and cold rolling.
基金Project supported by the National Natural Science Foundations of China(Grant No.51371089)the Foundation of National Key Basic Research and Development Program of China(Grant No.2010CB 631001)
文摘Nanocrystalline Cu film with a mirror surface finishing is prepared by the electric brush-plating technique. The as- prepared Cu film exhibits a superhydrophilic behavior with an apparent water contact angle smaller than 10°. A subsequent increase in the water contact angle and a final wetting transition from inherent hydrophilicity with water contact angle smaller than 90° to apparent hydrophobicity with water contact angle larger than 90° are observed when the Cu film is subjected to natural aging. Analysis based on the measurement of hardness with nanoindentation and the theory of the bond-order-length-strength correlation reveals that this wetting variation on the Cu film is attributed to the relaxation of residual stress generated during brush-plating deposition and a surface hydrophobization role associated with the broken bond polarization induced by surface nanostructure.