采用高能球磨法制备了用于热浸镀锌的纳米C eO2/Zn复合粉末,并利用X射线衍射(X-ray d iffraction,XRD)、X射线光电子能谱(X-ray photoe lectron spectroscopy,XPS)、透射电镜(T ransm iss ion e lectron m i-croscopy,TEM)、扫描电镜(Sc...采用高能球磨法制备了用于热浸镀锌的纳米C eO2/Zn复合粉末,并利用X射线衍射(X-ray d iffraction,XRD)、X射线光电子能谱(X-ray photoe lectron spectroscopy,XPS)、透射电镜(T ransm iss ion e lectron m i-croscopy,TEM)、扫描电镜(Scann ing e lectron m icroscopy,SEM)以及能谱分析(X-ray energy d ispers ive spec-trum,EDS)等方法,对复合粉末的显微结构、表面成分、晶粒大小、微观形貌以及元素分布进行了研究。结果表明,随着球磨时间的延长,纳米C eO2硬团聚体逐渐解聚,Zn晶粒不断细化,形成层片状复合粉末;球磨120 m in后纳米C eO2粒子分散良好,呈理想的单个均匀弥散分布状态包覆在Zn颗粒上形成近似球形的复合粒子,其粒径分布均匀。展开更多
The nanocomposite coating is obtained by electrochemical deposition of the zinc plating solution with ceria nanoparticles (mean diameter 30 nm). The effect of ceria nanoparticles on the electrodeposited zinc coating i...The nanocomposite coating is obtained by electrochemical deposition of the zinc plating solution with ceria nanoparticles (mean diameter 30 nm). The effect of ceria nanoparticles on the electrodeposited zinc coating is stu died by weight loss test, inductively copuled plasma quantometer (ICP), scanning electron microscopy (SEM) and X ray diffraction (XRD), respectively. It is found that under the same electrodeposition conditions, the corrosion resistance of the nanocomposite coating increases obviously while that of the micron composite coating only improves slightly; The ceria content of the nanocomposite coating is more than that of the micron composite coating. Ceria nanoparticles modify the surface morphology and crystal structure of the zinc matrix in correlation with the increase of corrosion resistance.展开更多
The hardness values and the wear resistance of Al2O3P/ Zn-Al composite, prepared by means of rheological casting technology,are investigated separately in this work. The results show that the addition of Al2O3P increa...The hardness values and the wear resistance of Al2O3P/ Zn-Al composite, prepared by means of rheological casting technology,are investigated separately in this work. The results show that the addition of Al2O3P increases the hardness values of the matrix at both room and high temperature and improves the wear resistance of the material.The hardness values and the wear resistance of the composite rise with the increase of the particle volume fraction or the decrease of the particle size.The raising of test temperature results in a rapid descending of its hardness values.However, the addition of Al2O3P improves the property of high temperature resistance of Zn-Al alloys significantly.Moreover,the effect of quenching, tempering or cycling heat treatment on the hardness values of the composite is also studied.展开更多
In order to improve the properties of ZA 27 and ZA4-3 zinc alloys and broaden their application ranges,SiC particlj1Ale composites, prepared by means of rheological casting technology, are investigated individually on...In order to improve the properties of ZA 27 and ZA4-3 zinc alloys and broaden their application ranges,SiC particlj1Ale composites, prepared by means of rheological casting technology, are investigated individually on their rT..t'llanical properties. The results of ne-cural strength, impact strensttl, compressive strength, hardness values and wear rate of the composites show that the addition of SiCp, leads to the increase of the compressive strength and hardness values at both room and higher temperature, and wear resistance of the materials, accompanying with the slight decrease of the fie-cural strength and sharp reduction of the impacttoughness. The factors affecting the mechanical properties of the composites are discussed in the paper.展开更多
文摘采用高能球磨法制备了用于热浸镀锌的纳米C eO2/Zn复合粉末,并利用X射线衍射(X-ray d iffraction,XRD)、X射线光电子能谱(X-ray photoe lectron spectroscopy,XPS)、透射电镜(T ransm iss ion e lectron m i-croscopy,TEM)、扫描电镜(Scann ing e lectron m icroscopy,SEM)以及能谱分析(X-ray energy d ispers ive spec-trum,EDS)等方法,对复合粉末的显微结构、表面成分、晶粒大小、微观形貌以及元素分布进行了研究。结果表明,随着球磨时间的延长,纳米C eO2硬团聚体逐渐解聚,Zn晶粒不断细化,形成层片状复合粉末;球磨120 m in后纳米C eO2粒子分散良好,呈理想的单个均匀弥散分布状态包覆在Zn颗粒上形成近似球形的复合粒子,其粒径分布均匀。
文摘The nanocomposite coating is obtained by electrochemical deposition of the zinc plating solution with ceria nanoparticles (mean diameter 30 nm). The effect of ceria nanoparticles on the electrodeposited zinc coating is stu died by weight loss test, inductively copuled plasma quantometer (ICP), scanning electron microscopy (SEM) and X ray diffraction (XRD), respectively. It is found that under the same electrodeposition conditions, the corrosion resistance of the nanocomposite coating increases obviously while that of the micron composite coating only improves slightly; The ceria content of the nanocomposite coating is more than that of the micron composite coating. Ceria nanoparticles modify the surface morphology and crystal structure of the zinc matrix in correlation with the increase of corrosion resistance.
文摘The hardness values and the wear resistance of Al2O3P/ Zn-Al composite, prepared by means of rheological casting technology,are investigated separately in this work. The results show that the addition of Al2O3P increases the hardness values of the matrix at both room and high temperature and improves the wear resistance of the material.The hardness values and the wear resistance of the composite rise with the increase of the particle volume fraction or the decrease of the particle size.The raising of test temperature results in a rapid descending of its hardness values.However, the addition of Al2O3P improves the property of high temperature resistance of Zn-Al alloys significantly.Moreover,the effect of quenching, tempering or cycling heat treatment on the hardness values of the composite is also studied.
文摘In order to improve the properties of ZA 27 and ZA4-3 zinc alloys and broaden their application ranges,SiC particlj1Ale composites, prepared by means of rheological casting technology, are investigated individually on their rT..t'llanical properties. The results of ne-cural strength, impact strensttl, compressive strength, hardness values and wear rate of the composites show that the addition of SiCp, leads to the increase of the compressive strength and hardness values at both room and higher temperature, and wear resistance of the materials, accompanying with the slight decrease of the fie-cural strength and sharp reduction of the impacttoughness. The factors affecting the mechanical properties of the composites are discussed in the paper.