Free-standing antiferroelectric Pb（Zr0.95Ti0.05O3（PZT（95/5）） thin film is fabricated on 200-nm-thick Pt foil by using pulsed laser deposition.X-ray diffraction patterns indicate that free-standing PZT（95/5） fil...Free-standing antiferroelectric Pb（Zr0.95Ti0.05O3（PZT（95/5）） thin film is fabricated on 200-nm-thick Pt foil by using pulsed laser deposition.X-ray diffraction patterns indicate that free-standing PZT（95/5） film possesses an α-axis preferred orientation.The critical electric field for the 300-nm-thick free-standing PZT（95/5） film transiting from antiferroelectric to ferroelectric phases is increased to 770 kV/cm,but its saturation polarization remains almost unchanged as compared with that of the substrate-clamped PZT（95/5） film.The energy storage density and energy efficiency of the substrate-clamped PZT（95/5） film are 6.49 J/cm^3 and 54.5%,respectively.In contrast,after removing the substrate,the energy storage density and energy efficiency of the free-standing PZT（95/5） film are enhanced up to 17.45 J/cm^3 and 67.9%,respectively.展开更多
基金supported by the National Natural Science Foundation of China(Grant Nos.11374312,51401230,and 51522105)the Fund for Ningbo Municipal Science and Technology Innovation Team,China(Grant No.2015B11001)
文摘Free-standing antiferroelectric Pb（Zr0.95Ti0.05O3（PZT（95/5）） thin film is fabricated on 200-nm-thick Pt foil by using pulsed laser deposition.X-ray diffraction patterns indicate that free-standing PZT（95/5） film possesses an α-axis preferred orientation.The critical electric field for the 300-nm-thick free-standing PZT（95/5） film transiting from antiferroelectric to ferroelectric phases is increased to 770 kV/cm,but its saturation polarization remains almost unchanged as compared with that of the substrate-clamped PZT（95/5） film.The energy storage density and energy efficiency of the substrate-clamped PZT（95/5） film are 6.49 J/cm^3 and 54.5%,respectively.In contrast,after removing the substrate,the energy storage density and energy efficiency of the free-standing PZT（95/5） film are enhanced up to 17.45 J/cm^3 and 67.9%,respectively.