Silicon nanocrystals synthesized by electron beam （e-beam） evaporation of Si and SiO2 mixture are studied. Rutherford backscattering spectrometry of the as-deposited Si-rich silicon dioxide or oxide （SRO） thin fil...Silicon nanocrystals synthesized by electron beam （e-beam） evaporation of Si and SiO2 mixture are studied. Rutherford backscattering spectrometry of the as-deposited Si-rich silicon dioxide or oxide （SRO） thin film shows that after evaporation, the Si and SiO2 concentration is well kept, indicating that the e-beam evaporation is suitable for evaporating mixtures of Si and SiO2. The SRO thin films are annealed at different temperatures for two hours to synthesize silicon nanoerystals. For the sample annealed at 1050℃, silicon nanoerystals with different sizes and the mean diameter of 4.5 nm are evidently observed by high resolution transmission electron microscopy （HRTEM）. Then the Raman scattering and photoluminescence spectra arising from silicon nanocrystals are further confirmed the above results.展开更多
基金Supported by the National Basic Research Program of China under Grant No 2006CB604904, 2009CB939703 and 2009CB939700 the National Natural Science Foundation of China under Grant Nos 60706023, 60676001, 90401002 and 90607022, Chinese Academy of Sciences under Grant No YZ0635, and the One-Hundred Talents Project of Chinese Academy of Sciences.
文摘Silicon nanocrystals synthesized by electron beam （e-beam） evaporation of Si and SiO2 mixture are studied. Rutherford backscattering spectrometry of the as-deposited Si-rich silicon dioxide or oxide （SRO） thin film shows that after evaporation, the Si and SiO2 concentration is well kept, indicating that the e-beam evaporation is suitable for evaporating mixtures of Si and SiO2. The SRO thin films are annealed at different temperatures for two hours to synthesize silicon nanoerystals. For the sample annealed at 1050℃, silicon nanoerystals with different sizes and the mean diameter of 4.5 nm are evidently observed by high resolution transmission electron microscopy （HRTEM）. Then the Raman scattering and photoluminescence spectra arising from silicon nanocrystals are further confirmed the above results.