This paper discusses the influence of Sb/In ratio on the transport properties and crystal quality of the 200 nm InAs_(x)Sb_(1-x)thin film.The Sb content of InAs_(x)Sb_(1-x)thin film in all samples was verified by HRXR...This paper discusses the influence of Sb/In ratio on the transport properties and crystal quality of the 200 nm InAs_(x)Sb_(1-x)thin film.The Sb content of InAs_(x)Sb_(1-x)thin film in all samples was verified by HRXRD of the symmetrical 004 reflections and asymmetrical 115 reflections.The calculation results show that the Sb component was 0.6 in the InAs_(x)Sb_(1-x)thin film grown under the conditions of Sb/In ratio of 6 and As/In ratio of 3,which has the highest electron mobility(28560 cm^(2)/V·s)at 300 K.At the same time,the influence ofⅤ/Ⅲratio on the transport properties and crystal quality of Al_(0.2)In_(0.8)Sb/InAs_(x)Sb_(1-x)quantum well heterostructures also has been investigated.As a result,the Al_(0.2)In_(0.8)Sb/InAs_(0.4)Sb_(0.6)quantum well heterostructure with a channel thickness of 30 nm grown under the conditions of Sb/In ratio of 6 and As/In ratio of 3 has a maximum electron mobility of 28300 cm^(2)/V·s and a minimum RMS roughness of 0.68 nm.Through optimizing the growth conditions,our samples have higher electron mobility and smoother surface morphology.展开更多
基金Supported by the Natural Science Basic Research Program of Shaanxi Province(2023-JC-QN-0758)Shaanxi University of Science and Technology Research Launch Project(2020BJ-26)Doctoral Research Initializing Fund of Hebei University of Science and Technology,China(1181476).
文摘This paper discusses the influence of Sb/In ratio on the transport properties and crystal quality of the 200 nm InAs_(x)Sb_(1-x)thin film.The Sb content of InAs_(x)Sb_(1-x)thin film in all samples was verified by HRXRD of the symmetrical 004 reflections and asymmetrical 115 reflections.The calculation results show that the Sb component was 0.6 in the InAs_(x)Sb_(1-x)thin film grown under the conditions of Sb/In ratio of 6 and As/In ratio of 3,which has the highest electron mobility(28560 cm^(2)/V·s)at 300 K.At the same time,the influence ofⅤ/Ⅲratio on the transport properties and crystal quality of Al_(0.2)In_(0.8)Sb/InAs_(x)Sb_(1-x)quantum well heterostructures also has been investigated.As a result,the Al_(0.2)In_(0.8)Sb/InAs_(0.4)Sb_(0.6)quantum well heterostructure with a channel thickness of 30 nm grown under the conditions of Sb/In ratio of 6 and As/In ratio of 3 has a maximum electron mobility of 28300 cm^(2)/V·s and a minimum RMS roughness of 0.68 nm.Through optimizing the growth conditions,our samples have higher electron mobility and smoother surface morphology.