We fabricate Sm-doped Ca3Co4O9+δ(CCO)bulk materials in magnetic field during both processes of chemical synthesis and cold pressing.The structure and electrical performance of the samples are investigated.With the in...We fabricate Sm-doped Ca3Co4O9+δ(CCO)bulk materials in magnetic field during both processes of chemical synthesis and cold pressing.The structure and electrical performance of the samples are investigated.With the increasing Sm concentration,the electrical conductivity 1/ρ decreases and the Seebeck coefficientαincreases.As a result,the power factor(PF=α^2/ρ)is raised slightly.After applying magnetic field,the extent of texture,grain size and density of all the bulk materials are improved obviously,thereby an enhanced electrical conductivity can be gained.Additionally,the degeneracy of Co^4+ state in the CoO2 layer of CCO is also increased as the magnetic field is used in the preparing process,which results in an enhancedα.The Ca2.85Sm0.15Co4O9+δ prepared in magnetic field shows the largest power factor(0.20 mW·m^-1·K^-2 at 1073 K).展开更多
基金Project supported by the National Natural Science Foundation of China(Grant No.51302055)。
文摘We fabricate Sm-doped Ca3Co4O9+δ(CCO)bulk materials in magnetic field during both processes of chemical synthesis and cold pressing.The structure and electrical performance of the samples are investigated.With the increasing Sm concentration,the electrical conductivity 1/ρ decreases and the Seebeck coefficientαincreases.As a result,the power factor(PF=α^2/ρ)is raised slightly.After applying magnetic field,the extent of texture,grain size and density of all the bulk materials are improved obviously,thereby an enhanced electrical conductivity can be gained.Additionally,the degeneracy of Co^4+ state in the CoO2 layer of CCO is also increased as the magnetic field is used in the preparing process,which results in an enhancedα.The Ca2.85Sm0.15Co4O9+δ prepared in magnetic field shows the largest power factor(0.20 mW·m^-1·K^-2 at 1073 K).