The structures of silicalite-1 and H、 Na form of ZSM-5 with various SiO2/Al2O3 ratios were characterized by powder XRD, 29Si MAS NMR, and the desorption process of р-xylene (p-x) on the zeolites was investigated by ...The structures of silicalite-1 and H、 Na form of ZSM-5 with various SiO2/Al2O3 ratios were characterized by powder XRD, 29Si MAS NMR, and the desorption process of р-xylene (p-x) on the zeolites was investigated by using TG/DTG/DTA. SiOH defects of ZSM-5 have no relation with the content of structural Al. Silicalite-1 possesses perfect framwork structure without SiOH defects and structural Al. On a curve of TG/DTG/DTA, p-x adsorbed by silicalite completely desorbs in the range of 57-174℃by two steps, accompaned with endothermal effect. While on the TG/DTG/DTA curves of H, Na-ZSM-5, there is a third desorption step of p-x in the range of 180-600℃ with exothermic effect. Below 180℃ the number of desorbed p-x molecules is related to pore space, but over 180℃，it is related to SiOH and positive ion linking with the structural Al.展开更多
文摘The structures of silicalite-1 and H、 Na form of ZSM-5 with various SiO2/Al2O3 ratios were characterized by powder XRD, 29Si MAS NMR, and the desorption process of р-xylene (p-x) on the zeolites was investigated by using TG/DTG/DTA. SiOH defects of ZSM-5 have no relation with the content of structural Al. Silicalite-1 possesses perfect framwork structure without SiOH defects and structural Al. On a curve of TG/DTG/DTA, p-x adsorbed by silicalite completely desorbs in the range of 57-174℃by two steps, accompaned with endothermal effect. While on the TG/DTG/DTA curves of H, Na-ZSM-5, there is a third desorption step of p-x in the range of 180-600℃ with exothermic effect. Below 180℃ the number of desorbed p-x molecules is related to pore space, but over 180℃，it is related to SiOH and positive ion linking with the structural Al.