A simple electrode preparation method is reported, based on the adsorption of poly-lysine on the surface of the gold electrode to immobilize CT-DNA through the electrostatic action. The DNA modified electrode is stabl...A simple electrode preparation method is reported, based on the adsorption of poly-lysine on the surface of the gold electrode to immobilize CT-DNA through the electrostatic action. The DNA modified electrode is stable during a 100 continuous cyclic voltammetric measurement.展开更多
The dependence of charge transfer resistances of electrodes in the aqueous Zn/V 2O 5 secondary battery on the Zn 2+ amount intercalated was studied by means of AC impedance experiments. The results showed that the ele...The dependence of charge transfer resistances of electrodes in the aqueous Zn/V 2O 5 secondary battery on the Zn 2+ amount intercalated was studied by means of AC impedance experiments. The results showed that the electrode reaction on cathode was controlled by the diffusion of Zn 2+ at the beginning of the discharge process. With the increase of Zn 2+ amount intercalated into the cathode, the reaction became a kinetic controlled process, i.e.a process controlled by intercalation of Zn 2+ in V 2O 5.展开更多
SiO2 glassy materials with Ge crystals embedded were formed by heating GeO2/SiO2 glass at 700 in the presence of hydrogen. GeO2/SiO2 glass was prepared with the sol-gel technique. The Ge/SiO2 samples show a special ph...SiO2 glassy materials with Ge crystals embedded were formed by heating GeO2/SiO2 glass at 700 in the presence of hydrogen. GeO2/SiO2 glass was prepared with the sol-gel technique. The Ge/SiO2 samples show a special photoluminescence property and exhibit strong luminescence at 392 nm（3.12 eV）, secondary strong luminescence at 600 nm（2.05 eV） and weak luminescence at 770 nm（1.60 eV） when excited under 246 nm（5.01 eV） ultra-violet light at room temperature. The structure of this new luminescence material was studied with XRD, XPS, and TEM. The results show that the presence of nanometer sized（around 10 nm） Ge and GeO crystals in the SiO2 may cause the three-band photoluminescence. The GeO2/SiO2 glass without going through the reducing process only has GeO2 in the SiO2 glass, and does not show the photo-（luminescence）.展开更多
文摘A simple electrode preparation method is reported, based on the adsorption of poly-lysine on the surface of the gold electrode to immobilize CT-DNA through the electrostatic action. The DNA modified electrode is stable during a 100 continuous cyclic voltammetric measurement.
文摘The dependence of charge transfer resistances of electrodes in the aqueous Zn/V 2O 5 secondary battery on the Zn 2+ amount intercalated was studied by means of AC impedance experiments. The results showed that the electrode reaction on cathode was controlled by the diffusion of Zn 2+ at the beginning of the discharge process. With the increase of Zn 2+ amount intercalated into the cathode, the reaction became a kinetic controlled process, i.e.a process controlled by intercalation of Zn 2+ in V 2O 5.
文摘SiO2 glassy materials with Ge crystals embedded were formed by heating GeO2/SiO2 glass at 700 in the presence of hydrogen. GeO2/SiO2 glass was prepared with the sol-gel technique. The Ge/SiO2 samples show a special photoluminescence property and exhibit strong luminescence at 392 nm（3.12 eV）, secondary strong luminescence at 600 nm（2.05 eV） and weak luminescence at 770 nm（1.60 eV） when excited under 246 nm（5.01 eV） ultra-violet light at room temperature. The structure of this new luminescence material was studied with XRD, XPS, and TEM. The results show that the presence of nanometer sized（around 10 nm） Ge and GeO crystals in the SiO2 may cause the three-band photoluminescence. The GeO2/SiO2 glass without going through the reducing process only has GeO2 in the SiO2 glass, and does not show the photo-（luminescence）.