水凝胶固态电解质有效避免了液态电解质易泄漏和难以封装的问题,使柔性可穿戴的便捷式供电设备成为可能。将MXene纳米片嵌入由丙烯酰氧乙基三甲基氯化铵(DMAEA-Q)和苯乙烯磺酸钠(NaSS)组成的聚两性离子水凝胶基质中,制备MXene/聚两性离子水凝胶。MXene作为物理交联剂和导电填料可以提高水凝胶的导电性,将其组装锌空气电池,电池保持较好的功率密度(50 mW/cm^(2))、比容量(753.1 mAh/g)和250次以上的长时间充放电循环寿命。
The hydrogel solid-state electrolyte effectively avoids the problems of easy leakage and difficult en⁃capsulation of liquid electrolyte,making it possible to use flexible and wearable portable power supply devices.MXene/polyzwitterionic hydrogel is prepared by embedding MXene nanosheets into a polyzwitterionic hydrogel matrix consisting of acryloyloxyethyltrimethylammonium chloride(DMAEA-Q)and sodium styrenesulfonate(NaSS).MXene can be used as a physical crosslinker and conductive filler to improve the conductivity of hydro⁃gels,and the results show that the battery maintains a good power density(50 mW/cm^(2)),specific capacity(753.1 mAh/g)and a long charge-discharge cycle life of more than 250 cycles.
作者
张思瑶
孙元娜
杜莹
王东宇
汪俊
杨佳航
吕桂鑫
秦佳欣
ZHANG Siyao;SUN Yuanna;DU Ying;WANG Dongyu;WANG Jun;YANG Jiahang;LYU Guixin;QIN Jiaxin(School of Materials Science and Engineering,Xi′an Key Laboratory of Textile Composite Materials,Xi′an Polytechnic University,Xi′an 710048,China)
出处
《印染》
CAS
北大核心
2024年第10期19-23,共5页
China Dyeing and Finishing
基金
大学生创新创业训练计划项目(S202310709023)
陕西省高校科协青年人才托举计划项目(20210421)
西安市纺织复合材料重点实验室科技指导性项目(xafzfc-zd05)。
作者简介
张思瑶(2002-),女,硕士研究生;通信作者:孙元娜(1987-),女,西安工程大学副教授,博士研究生,研究方向为智能高分子水凝胶材料设计与研发。E-mail:sunyuanna@xpu.edu.cn。