摘要
以甲基丙烯酸缩水甘油酯为单体 ,二乙烯苯 /三烯丙基异氰脲酸酯作为混合交联剂 ,甲苯和正庚烷为混合致孔剂 ,通过悬浮聚合 ,合成了一系列 GMA-DVB-TAIC大孔共聚物 ,考察了不同反应阶段共聚物的孔结构 ,通过调节交联剂的用量、致孔剂的用量和比例 ,可以得到具有较大孔容和孔径、较高热稳定性和性能优良的
A series of macroporous glycidyl methacrylate triallyl isocyanurate divinylbenzene(GTD) copolymers were synthesized with toluene and n heptane as the porogenic agent by suspension copolymerization.Some of them should be used as adsorbents for hemoperfusion.The effects of the amount of crosslinking agent and mixed porogenic agent on structural property, such as specific area, average pore diameter, pore volume and porosity were investigated.